Spesifikasi:
Type: Acrylic paint
Color : White
Film appearance : Matt
Specific gravity : 1.28 ± 0.02
Solid by volume : 34 ± 2 %
Solid by weight : 52 ± 2 %
Flash point : N/A
Wet film thickness : 100 - 110 microns
Dry film thickness : 35 - 40 microns
Practical coverage: 35 - 45 m 2/ Gal
Remark : Actual Surface coverage will depend on surface irregularities, Mixing, Application Condition
method and technique; as well as the structure and dimensions of the object to be coated.
APPLICATION
Tools : Air spray, Brush, Roller
Thinner : Water
Dilution : 10- 15% by volume for Roller or Brush
: 20- 25% by volume for Spray
APPLICATION SYSTEM:
Surface Preparation
New Surface concrete : Substrate must be completely cured and dried (~1 month) free from oil, grease and mildew
At a crack width less than 1 mm and not break continuity, Putty for filling with TOA acrylic filler.
Around the crack wider than 1 mm or a different continuity, Putty for filling with TOA Acrylic Sealant.
Old Surface concrete : Powdery and chalky surface must be scrubbed and cleaned with water.
Fungus and mildew growth must be cleaned off. Left to dry for 2-3 days.
For more smooth surface use TOA Acrylic Wall Filler for skim coating.
Structure Coating Surface : The surface must be clean, dry, free of loose rust and scale paint, etc. Remove all oil, grease and other
contaminants with a suitable solvent. Metal should be blast cleaned in accordance with
NACE No.2 / SSPC-SP10, ISO 8501:1, SIS Sa 2.5 to a near-white finish using a suitable abrasive
or power tool cleaning in accordance with SIS St 3 or SSPC-SP3 .
: Surface repair (cracks, pores, holes) done with TOA Epoxy putty and polishing of surface with
moltoprene disk.
: Remover all oil, grease, dirt, oxide and other foreign material by cleaning per SSPC-SP1,
Solvent Cleaning before coating.
: To prevent the formation of rust or oxide, coat as soon as possible after cleaning.
For maximum protection, the coating must have direct contact with the metal surface.
Coating System
Protective Coating : Primer Supershield Aqua Gloss Primer 40 microns x 1 coat
: Topcoat Supershield Aqua Gloss 40 microns x 2 coats
Recommendation : The proper relative humidity in the work shall not exceed 85% RH.
: The temperature of the substrate should be minimum 10 ????C and at least 3 ????C above the dew point of the air ,
temperature and relative humidity measured in the vicinity of the substrate for prevent moisture and water drop
on substrate effective adhesion and drying time.
Dimensi:
Deskripsi:
FEATURES:
Supershield Aqua Gloss Primer is a primer base on acrylic emulsion resin and corrosion- inhibiting zinc
phosphate pigment.It is characterized with strong adhesion to concrete, steel, galvanized and wood.
As a rust preventing primer on steel structures,
It is suitable of being top coated by most solventborne coatings.